Stress-Strain Analysis of the Fretting and Non-Fretting Steel Wire: An Experimental and Simulation Study
DOI:
https://doi.org/10.18311/jmmf/2024/43764Keywords:
Breaking Load, Fretting Wear, Tensile Stress, Tensile Strain, Wear Scar, WireAbstract
Fretting wear is one of the main degradation mechanisms produced in steel wire and it is widely used for the lifting and handling of equipments. The main objective of the present work is to analyse the mechanical properties of the fretting and non-fretting wire. Statics tensile tests were performed on non-fretting wire and pre-damaged artificially fretting wire subsequently, after that tensile stress (σT), tensile strain (εT), and breaking load (BL) were measured for both wires and their basic mechanical properties were compared. For the analysis wire diameter values varies from 7 mm to 9 mm and artificially pre-damaged wire having reduced diameters varies from 5.8 mm to 8.1 mm were used. From these tests the basic mechanical properties values of maximum tensile stress, tensile strain, modulus of elasticity (E), breaking load (BL) 1610 N/mm2, 12.08%, 78854.3 Mpa and 56.73 KN respectively were obtained, for pre-damaged artificially fretting wire. On the other hand, for the non-fretting wire, the values of maximum tensile stress, tensile strain, modulus of elasticity, and breaking load have been obtained as 1171.5 MPa,16.40 %,63289.4 MPa and 58.7 KN respectively.
Downloads
Metrics
Downloads
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Accepted 2024-07-25
Published 2024-08-19
References
Dickinson HW. A Condensed History of Rope-king. Trans. Newcom Soc. 1942; 23(1):71-91. https://doi.org/10.1179/tns.1942.007
Clarke RC. The history of hemp in Norway. J Ind Hemp. 2002; 7(1):89-103. https://doi.org/10.1300/J237v07n01_08
Costello GA. Theory of wire rope. Berlin: Springer; 1997. https://doi.org/10.1007/978-1-4612-1970-5
Cruzado A, Hartelt M, Wäsche R, Urchegui MA, Gómez X. Fretting wear of thin steel wires. Part 1: Influence of contact pressure. Wear. 2010; 268(1): 1409-16. https://doi.org/10.1016/j.wear.2010.02.017
Cruzado A, Hartelt M, Wäsche R, Urchegui MA, Gómez X. Fretting wear of thin steel wires. Part 2: Influence of crossing angle. Wear. 2011; 273(1): 60-9. https://doi.org/10.1016/j.wear.2011.04.012
Shen Y, Zhang D, Duan J, Wang D. Fretting wear behaviors of steel wires under friction-increasing grease conditions. Tribol Int. 2011; 44(11):1511-17. https://doi.org/10.1016/j.triboint.2010.10.021
Wang D, Zhang D, Ge S. Fretting-fatigue behavior of steel wires in low cycle fatigue. Materials and Des. 2011; 32(10) :4986-93. https://doi.org/10.1016/j.matdes.2011.06.037
Wang D, Zhang D, Ge S. Effect of displacement amplitude on fretting fatigue behavior of hoisting rope wires in low cycle fatigue. Tribol Int. 2012; 52:178-189. https://doi.org/10.1016/j.triboint.2012.04.008
Cruzado A, Leen SB, Urchegui MA, Gómez X. Finite element simulation of fretting wear and fatigue in thin steel wires. Int J Fatigue. 2013; 55: 7-21. https://doi.org/10.1016/j.ijfatigue.2013.04.025
Cruzado A, Urchegui MA, Gómez X. Finite element modelling of fretting wear scars in the thin steel wires: application in crossed cylinder arrangements. Wear. 2014; 318(2):98-105. https://doi.org/10.1016/j.wear.2014.06.019
Peterka P, Krešák J, Kropuch S, Fedorko G, Molnar V, Vojtko M. Failure analysis of hoisting steel wire rope. Engg Fail Anal. 2014; 45:96-105. https://doi.org/10.1016/j.engfailanal.2014.06.005
Wang D, Zhang D, Zhao W, Ge S. Quantitative analyses of fretting fatigue damages of mine rope wires in different corrosive media. Mater Sci. Engg. 2014; 596:80-88. https://doi.org/10.1016/j.msea.2013.12.047
Chen Y, Meng F, Gong X. Inter wire wear and its influence on contact behavior of wire rope strand subjected to cyclic bending load. Wear. 2016; 368: 470-484. https://doi.org/10.1016/j.wear.2016.10.020
Wang D, Li X, Wang X, Zhang D. Dynamic wear evolution and crack propagation behaviors of steel wires during fretting-fatigue. Tribol Int. 2016; 101:348-55. https://doi.org/10.1016/j.triboint.2016.05.003
Wokem C, Joseph T, Curley M. Fatigue life prediction for cables in cyclic tension. J. Strain Anal Engg Des. 2018; 53:141-15583. https://doi.org/10.1177/0309324717753211
Ren Z, Lu Z, Yu Q, Jiang Y. Failure analysis and safety protection of a certain type of wire ropes under high-speed impact loads. In: MATEC web of conferences. 2018; 142: EDP Sciences. https://doi.org/10.1051/matecconf/201714203001
Wang X, Wang D, Zhang D, Ge S, Araújo JA. Effect of torsion angle on tension-torsion multiaxial fretting fatigue behaviors of steel wires. Int J Fatigue. 2018; 106:159-16485. https://doi.org/10.1016/j.ijfatigue.2017.09.021
Zhang D, Yang X, Chen K, Zhang Z. Fretting fatigue behavior of steel wires contact interface under different crossing angles. Wear. 2018; 52:61-86. https://doi.org/10.1016/j.wear.2017.12.014
Wang X, Wang D, Li X, Zhang D, Ge S, Araújo JA. Comparative analyses of torsional fretting, longitudinal fretting and combined longitudinal and torsional fretting behaviours of steel wires. Engg Fail Anal. 2018; 85:116-12587. https://doi.org/10.1016/j.engfailanal.2017.12.002
Zhang J, Wang D, Zhang D, Ge S, Araújo JA. Dynamic contact and slip characteristics of bent hoisting rope in coal mine. Journal of the Brazilian Society of Mechanical Sciences and Engineering. 2018; 40(3):12089. https://doi.org/10.1007/s40430-018-1044-5
Peng YX, Chang XD, Sun SS, Zhu ZC, Gong XS, Zou SY, XuWX, Mi ZT. The friction and wear properties of steel wire rope sliding against itself under impact load. Wear. 2018; 400:194-20690. https://doi.org/10.1016/j.wear.2018.01.010
Chang XD, Peng YX, Zhu ZC, Gong XS, Yu ZF, Mi ZT, Xu CM. Experimental investigation of mechanical response and fracture failure behavior of wire rope with different given surface wear. Tribol Int. 2018; 119:208-21. https://doi.org/10.1016/j.triboint.2017.11.004
American Society of Testing Materials (ASTM). Standard test methods for tension testing of metallic materials. ASTM International Headquarters, 100 Barr Harbor Drive, West Conshohocken, USA; 2013. p. 19428-2959.
Dubey SP, Manish D, Uttarwar, Tiwari MS. Reliability study of 42 cum rope shovel under diverse geo-mining parameters: A case study. J Mines Met Fuels. 2016; 105-22.